Nm400 Nm500 Bulletproof Wear Resistant Steel Plate/Armor Plate
Posted on

Model NO.: steel plate
Special Use: High-strength Steel Plate, Wear Resistant Steel
Application: Mining Machiner/Armor Plate/Heavy Duty Machine
Hardness Range: 360hb-600hb
Cutting Service: Avaliable
Bending Service: Avaliable
Hard 500: Hard 400
Armor Steel Plate: Ballistic Plate
Trademark: Shandong
Transport Package: Seaworth Packaging
Specification: thickness: 4.5-150mm
Origin: China
Model NO.: steel plate
Special Use: High-strength Steel Plate, Wear Resistant Steel
Application: Mining Machiner/Armor Plate/Heavy Duty Machine
Hardness Range: 360hb-600hb
Cutting Service: Avaliable
Bending Service: Avaliable
Hard 500: Hard 400
Armor Steel Plate: Ballistic Plate
Trademark: Shandong
Transport Package: Seaworth Packaging
Specification: thickness: 4.5-150mm
Origin: China

Ar400 Ar500 Wear Resistant Plates/Armor Steel Plate/Ballistic Plate

Bulletproof wear resistant steel plate
Wear  Resistant  Steel plate
Abrasion Resisant Plate AR400 AR500
Hard steel plate
hard 500 hard 400
steel plate cutting and bending
Product Descrition
  1. Production Process
1)Steelmaking process Flow Chart
Blast  Furance+Hot Metal Ladle Truck+KR Hot Metal Treatment+Converter+LF Refining Furnace+RH Vacuum Degassing Furance+Con-cast

2.Rolling Process Flow Chart
Reheating Furance+High-pressure Water Descaling+Edger Mill+Roughing Mill+Finishing Mill+Accelerated cooling+Hot Leveler+Marking and Spray Printing+Cooling Bed+On-line UT+Crop Shear+Double-side Trimming Shear+Cut-to-length Shear+Measurement+Marking and Spray Printing+Cold Leveler/Heat treatment

3.Heat-Treatment Flow Chart
Plate+Shot Blasting+Quenching Furance+Quenching Machine+Tempering Furance+Warm Leveler+Cooling Bed+Cutting+Cold Leveler+Finishing&Packaging

4.Thickness  and  Width
Thickness:4.5mm-150mm
Width:1600mm-4100mm

5.Main Grade
Germany:XAR400,XAR450,XAR500,XAR600,Dillidur400,Dillidur500
Belgium:QUARD400,QUARD450,QUARD500
France:FORA400,FORA500,Creusabro4800,Creusabro8000
Baosteel:B-HARD360,B-HARD400,B-HARD450,B-HARD500
HBIS:NM360,NM400,NM450,NM500
Finland:RAEX400,RAEX450,RAEX500
Japan:JFE-EH360,JFE-EH400,JFE-EH500,WEL-HARD400,WEL-HARD500

6.Chemical Composition&Property
Grade c Si Mn P S Al Cr+Ni+Mo Nb+V+Ti
NM400 0.10-0.40 0.20-0.40 1.00-2.00 Max 0.015 Max 0.003 Min 0.020 Max 0.9 Trace Amount
NM450 0.10-0.40 0.20-0.40 1.00-2.00 Max 0.015 Max 0.003 Min 0.020 Max 1.2
NM500 0.10-0.40 0.20-0.45 1.00-2.00 Max 0.015 Max 0.003 Min 0.020 Max 1.5
NM550 0.10-0.50 0.20-0.45 1.00-1.50 Max 0.015 Max 0.003 Min 0.020 Max 2.0
NM600 0.10-0.50 0.20-0.45 1.00-1.50 Max 0.015 Max 0.003 Min 0.020 Max 2.5
XCHD400 0.10-0.30 0.20-0.40 1.00-2.00 Max 0.015 Max 0.003 Min 0.020 Max 0.1
XCHD450 0.10-0.40 0.20-0.40 1.00-2.00 Max 0.015 Max 0.003 Min 0.020 Max 0.9
XCHD500 0.10-0.40 0.20-0.45 1.00-2.00 Max 0.015 Max 0.003 Min 0.020 Max 1.5
 
7.
 
Grade Size(mm) RP0.2(Mpa) Rm(Mpa) A50(%) AKV,(ºC) KV2(J) HBW
NM400 100 1233 1337 15 -20 35 37 42 415
NM450 60 1345 1434 9.5 -20 72 59 58 455
NM500 50 1608 1706 10.5 -20 43 50 45 495
XCHD400 35 1025 1161 17.5 -40 52 45 40 413
XCHD450 30 1281 1400 10.5 -40 45 48 52 453
XCH500 6 1465 1529 13.5 -40 24 24 22 515
 
8.Cerifications
9 Classification Society
ISO 9001 Certified
 
9.Packaging&Shipping
Seaworthy packaging  by  container  or bulk cargo vessel
Delievery time:stock size within 7days;new material within 40days
10.Our services
We    can  cut  and bend steel plate  according  to customer's requriement or drawing,packaging according  to customers' request
11.Application
By adopting the combined chemical composition design of low carbon,low sulfur,low phosphorous and micro-alloy,by applying the offline quenching and other advanced automation technologies,our wear resistant(Abrasion Resisant) plate are popular at home and abroad. Mainly used for thermal Power plant,Coal Mines ,Cement Mills,Loading Machinery,Mining Machinery,Project Machinery.Metallurgical Machinery,Wear resistant plate also can be applied in Sand Mill Cylindrical Shell, Vane, Mechanical Parts used in yard and port, Bearing Structure Parts etc.

12.Our armor steel plate testing results in different thickness
 
Testing results of wear resistant steel plates
Grade Thickness(mm) Hardness/HB Tenslile strength/MPA Enlongation -20ºC Longitudinal Impact Value/J
NM400 6 406 1280 16 76/87/65
NM400 20 404 1260 17.5 57/57/65
NM400 50 398 1300 25.5 40/35/45
NM400 80 417 1320 23.5 48/51/49
NM450 6 439 1320 23 43/38/30
NM450 20 448 1460 24 62/52/66
NM450 50 444 1340 21 35/37/40
NM450 80 454 1410 21.5 40/41/49
NM500 6 485 1653 11.5 33/26/32
NM500 20 505 1730 17.5 36/33/30
NM500 50 499 1569 16.5 42/38/32
NM500 70 488 1540 12.5 60/55/64
NM550 6 540 1853 10.5 /
NM550 20 545 1855 11.5 /
NM550 50 550 1900 10.5 /
NM550 70 545 1840 12 /
NM600 6 575 / / /
NM600 20 580 / / /
NM600 50 582 / / /
NM600 70 578 / / /
 Keywords:Hard steel plates/AR500 wear resistant steel plate/NM400 NM500 wear resistant steel plates/armor steel plate/ballistic plates/bulletproof steel plate/Hard steel plates/AR500 wear resistant steel plate/NM400 NM500 wear resistant steel plates/armor steel plate/ballistic plates/bulletproof steel plate/Hard steel plates/AR500 wear resistant steel plate/NM400 NM500 wear resistant steel plates/armor steel plate/ballistic plates/bulletproof steel plate

Our wear resistant steel plate steel melting
Nm400 Nm500 Bulletproof Wear Resistant Steel Plate/Armor Plate
Nm400 Nm500 Bulletproof Wear Resistant Steel Plate/Armor Plate
Nm400 Nm500 Bulletproof Wear Resistant Steel Plate/Armor Plate
Nm400 Nm500 Bulletproof Wear Resistant Steel Plate/Armor PlateNm400 Nm500 Bulletproof Wear Resistant Steel Plate/Armor Plate

Ar400 Ar500 Wear Resistant Plates/Armor Steel Plate/Ballistic Plate

Bulletproof wear resistant steel plate
Wear  Resistant  Steel plate
Abrasion Resisant Plate AR400 AR500
Hard steel plate
hard 500 hard 400
steel plate cutting and bending
Product Descrition
  1. Production Process
1)Steelmaking process Flow Chart
Blast  Furance+Hot Metal Ladle Truck+KR Hot Metal Treatment+Converter+LF Refining Furnace+RH Vacuum Degassing Furance+Con-cast

2.Rolling Process Flow Chart
Reheating Furance+High-pressure Water Descaling+Edger Mill+Roughing Mill+Finishing Mill+Accelerated cooling+Hot Leveler+Marking and Spray Printing+Cooling Bed+On-line UT+Crop Shear+Double-side Trimming Shear+Cut-to-length Shear+Measurement+Marking and Spray Printing+Cold Leveler/Heat treatment

3.Heat-Treatment Flow Chart
Plate+Shot Blasting+Quenching Furance+Quenching Machine+Tempering Furance+Warm Leveler+Cooling Bed+Cutting+Cold Leveler+Finishing&Packaging

4.Thickness  and  Width
Thickness:4.5mm-150mm
Width:1600mm-4100mm

5.Main Grade
Germany:XAR400,XAR450,XAR500,XAR600,Dillidur400,Dillidur500
Belgium:QUARD400,QUARD450,QUARD500
France:FORA400,FORA500,Creusabro4800,Creusabro8000
Baosteel:B-HARD360,B-HARD400,B-HARD450,B-HARD500
HBIS:NM360,NM400,NM450,NM500
Finland:RAEX400,RAEX450,RAEX500
Japan:JFE-EH360,JFE-EH400,JFE-EH500,WEL-HARD400,WEL-HARD500

6.Chemical Composition&Property
Grade c Si Mn P S Al Cr+Ni+Mo Nb+V+Ti
NM400 0.10-0.40 0.20-0.40 1.00-2.00 Max 0.015 Max 0.003 Min 0.020 Max 0.9 Trace Amount
NM450 0.10-0.40 0.20-0.40 1.00-2.00 Max 0.015 Max 0.003 Min 0.020 Max 1.2
NM500 0.10-0.40 0.20-0.45 1.00-2.00 Max 0.015 Max 0.003 Min 0.020 Max 1.5
NM550 0.10-0.50 0.20-0.45 1.00-1.50 Max 0.015 Max 0.003 Min 0.020 Max 2.0
NM600 0.10-0.50 0.20-0.45 1.00-1.50 Max 0.015